Q1: لماذا يكون الزركونيا أخضر بعد التلبيد؟
A1:It is because your finance has been polluted, different types of zirconia have different subsidiary substances during production. when sintering the substance will get rid of zirconia and come to the heart of finance, it made the heart of finance was polluted because the substance doesn't get rid of completely.
Pls, sinter the finance empty immediately to help the substance get rid of completely. Each time sintering the heating elements will have new crystalline film. It is better to change the sintering tray and beads as well.
نصائح لتجنب التلوث:
1 ، لا تلبد أنواع مختلفة من الزركونيا بشكل مستمر.
على سبيل المثال ، الكتل البيضاء الملبدة اليوم ، إذا كنت بحاجة غدًا إلى كتل مظللة مسبقًا ، فيجب عليك تلبيد التمويل فارغًا بعد كتل بيضاء ثم تلبيدها مظللة مسبقًا.
2 ، يجب تجفيف جميع تيجان الكتل البيضاء 200 درجة قبل التكلس بـ 30 دقيقة
Q2: ما الفرق بين SHT Multilayer و 3D - Plus Multilayer؟
A2: SHT هو تدرج لوني. القوة 1200 ميجا باسكال و 45 في المائة شفافة.
ثلاثي الأبعاد - زائد هو تدرج لوني للون وقوة. القوة من 600 ميجا باسكال إلى 900 ميجا باسكال ، الشفافية من 43 بالمائة إلى 49 بالمائة.
في غضون ذلك ، نحن بصدد اختبار 3D E - زائد ، يمكن أن تكون القوة 1100 كحد أقصى والشفافية من 47 بالمائة إلى 49 بالمائة.
Q3: كسر جسري بعد التزجيج؟
ج 3: هناك احتمالان لهذه المشكلة:
1. The upper gingival porcelain requires repeated enamels, and the burned bridge undergoes multiple heating and cooling. Pulling and cracking are caused by the too fast cooling rate.
Suggestions: Lower the cooling rate and reduce the number of times porcelain loading
Porcelain furnace cooling program should be set a little slower, porcelain furnace cooling too fast will cause thermal stress, thermal shock, ceramics are most afraid of rapid cooling and heating, porcelain furnace cooling down a little bit, the lower temperature limit is set a little lower
This needs to be paid attention to in the porcelain furnace, the mouthful of rapid cold causes thermal stress cracking
Generally, the teeth in the porcelain furnace come out at 700 degree and come into contact with the air, and the teeth at 700 degree encounter the cold air at 25 degree , which causes cracking.
Easiest to break from the missing position, because the missing position is solid, accumulates more heat, and dissipates slowly
2. When the porcelain is cut, the teeth are cut vertically with fine slices. (In the past, metal teeth and porcelain teeth were cut in this way, so technicians are used to it).
Suggestion: When the car porcelain is cut between the teeth, it should be cut sideways in the direction of the teeth. However, this possibility is generally small.